Arena Petro Gas

RG 1102 XK<br />
POLYPROPYLENE HOMOPOLYMER<br />
RG 1102 XK is a Homopolymer with low water carry over and preferred grade for tapes.<br />
PROCESSING METHOD : Extrusion<br />
APPLICATION : Raffia, tape yarn, technical textiles, carpet backing, diary products<br />
PropertyTest MethodUnitValue<br />
MFR ( 230˚ C/ 2.16 Kg )ASTM D1238/Lgr/10min4<br />
Tensile Modulus of Elasticity<br />
(1mm/min)ASTM D638MPa1500<br />
Tensile Strength at Yield<br />
(50mm/min)ASTM D638MPa34<br />
Elongation at Yiel<br />
(50mm/min)ASTM D638%9<br />
Notched Charpy Impact at 23˚ISO 179/ 1eAKJ/m24<br />
Notched Charpy Impact at -30˚ISO 179/ 1eAKJ/m21.7<br />
Vicat Softening Point, 10NASTM D1525˚C154<br />
Ball indentation hardnessISO 2039-1MPa74<br />
HDT ( 0.46 N/mm2 )ASTM D648˚C85<br />
Melting Point , DSCASTM D3417˚C163<br />
DensityASTM D792gr/cm30.91<br />